ERW炭素鋼熱交換器およびコンデンサーチューブ

製品説明

TORICH ASTM A214 ERW炭素鋼熱交換器およびコンデンサーチューブ

Standard	ASTM A214, A450
Matrial	Q195, Q215, Q235 etc Carbon Steel
Size	OD: 6.76.2mm WT: 1-20mm Length: 1-12m
Manufacture	Tubes are made by electric-resistance welding.
Surface Condition	The finished tubes are free of scale., slight amount of oxidation is not considered as scale
Hardness Requirements	The tubes shall have a hardness number not exceeding 72HRB.
Thermal Treatment:	After welding, all tubes are heat treated at a temperature of 1200℉(650℃) or higher and following by cooling in air or in a cooling chamber of a controlled atmosphere furnace. Cold drawn tubes shall be heat treated after the final cold-draw pass at a temperature of 1200℉(650℃) or higher
Test and Inspection	- Flattening Test - Flange Test - Reverse Test - Hydrostatic or Nondestructive Electric Test

ODとWTの許容差（SA-450 / SA-450M）

OD in (mm)	+	-	WT in (mm)	+	-
<1" (25.4)	0.10	0.10	≤1.1/2" (38.1)	20%	0
1"~1.1" (25.4-38.1)	0.15	0.15	≤1.1/2" (38.2)	20%	0
>1.1/2"~<2" (38.1-50.8)	0.20	0.20
2"~<2.1/2" (50.8-63.5)	0.25	0.25
2.1/2"~<3" (63.5-76.2)	0.30	0.30
3"~<4" (76.2-101.6)	0.38	0.38
4"~<7.1/2" (101.6-190.5)	0.38	0.64
>7.1/2"~9" (190.5-228.6)	0.38	1.14

化学的要求

C	0.18
Mn	0.27 to 0.63
P	≤0.035
S	≤0.035

プロダクションショー

1.到着する原材料の検査
2.スチールグレードの混合を避けるための原料の分離
3.冷間引抜きのための加熱およびハンマー締め
4.冷間引抜きおよび冷間圧延、オンライン検査
5.熱処理、+ A、+ SRA、+ LC、+ N、Q + T
6.特定の長さにまっすぐに切断 - 完成測定検査
7.引張強さ、降伏強さ、伸び、硬度、衝撃、Mictrostrutureなどを含む自分のラボでの機械的試験
8.パッキングとストッキング

当社の鋼管の100％が寸法検査されています
当社の鋼管の100％が肉眼で確認され、完全な表面状態と表面欠陥がないことが保証されます。
100％渦電流試験および超音波検査を使用して縦方向および横方向の欠陥を除去する。

よくある質問

Q：あなたは貿易会社か製造業者ですか？

A：専門の鋼管材料の発明者、製造業者およびソリューションプロバイダー

Q：納期はどのくらいですか？
A：商品が在庫されている場合、通常は7〜14日です。商品が入荷していない場合は30〜60日ですが、数量に応じています。

Q：カーボンシームレス鋼管のサンプルを提供していますか？それは無料ですか、余分ですか？
A：はい、無料でサンプルを提供できますが、貨物料金を支払う必要があります。

Q：お支払いの条件は？
A：お支払いは、<1000USD、100％事前に。お支払い> = 1000USD、事前に30％T / T、配送前にバランス。

別の質問がある場合は、plsまでお気軽にお問い合わせください

TORICH ASTM A214 ERW炭素鋼熱交換器およびコンデンサーチューブ